牌号简介 About |
---|
Ebarta lh 28-1是一种双组分环氧复合树脂,在室温下预固化,根据后固化的不同,可使用到175°C。由于该复合树脂系统不含填料,因此具有良好的润湿性能,并使玻璃纤维含量高成为可能。这导致了低热膨胀系数和高强度。与铝颗粒一起,Ebarta LH 28-1适用于耐热模具和模具的背面填充。在室温下固化需要7天,材料只能用于60°C的应用。应用真空成型工具预浸工具热粘合工具吹塑模具聚酯注塑模具聚酯冲压工具性能非常高,取决于后固化到175°C长的处理时间低放热特性热固化 ebalta LH 28-1 is a two components epoxy laminating resin, precuring at room temperature and, depending on postcuring, can be used till 175°C. Since this laminating resin system contains no fillers, it has got good wetting properties and makes a high glass fabric content possible. This leads to a low coefficient of thermal expansion and high strength. Together with aluminium granules, ebalta LH 28-1 is suitable for back filling of heat resistant moulds and moulding tools. At room temperature the curing takes 7 days and the material can only be used for applications till 60°C. Applications Vacuum forming tools Prepreg tools hot gluing tools Blow moulds Polyester injection moulds Polyester press tools Properties very high heat resistance, depending on post curing till 175°C long processing time low exothermic character heat curing |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
10 到 22 | kJ/m² | ISO 179 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.07 到 1.13 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
0.65 到 0.85 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
24 到 48 | hr | |
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
240 到 360 | min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
弯曲应变 Bending strain |
% | ISO 178 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
后固化时间 Post curing time |
|||
40℃ 40℃ |
hr | ||
60℃ 60℃ |
hr | ||
100℃ 100℃ |
hr | ||
135℃ 135℃ |
hr | ||
160℃ 160℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |
【新闻资讯】查看全部
索尔维特种聚合物可承受强腐蚀性的麦瑞斯医用表面消毒剂
2021-03-07 搜料网资讯: 2021年2月26日,索尔维与物体表面消毒产品的领导者麦瑞斯(Metrex)宣布了索尔维的几款先进医用级材料与麦瑞斯消毒剂的相容性研究结果。这次联合研究使用麦瑞斯的最新 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |